High Cr White Iron wear resistant and higher hardness Castings blow bars shipment to American for ball mill
Summarization
High Cr white iron material possess a combination of superior abrasion resistance and a reasonable
degree of toughness. The high Cr castings have longer service life than the other material,such as
high Mn steel and Cr-Mo alloy steel.And now it is widely used in the working condition of high wear and low impact,such as dry grinding process,coal mills,cement mills due to its excellent performance.
Quick Description
Material:High Cr Cast Iron
Hardness:More than HRC58
Impact Value:≥AK10J
Dimension:As per drawing
Heat Treatment Process:Quenching and Tempering
Casting Process:Sand Casting
Application:Coal Mill,Cement Mill,Mining Industry etc.
Package:Steel Pallets
Delivery Time:Depends on the quantity to be ordered.
MOQ:2Tons
Technical Parameters
| Item | High Cr White Iron | High Cr Alloy Steel | High Mn Steel | Ni-hard Cast Iron |
| C | 2.4-3.2 | 1.1-2.2 | 0.9-1.3 | 2.4-3.6 |
| Si | 0.6-1.2 | 0.6-1.2 | ≤0.8 | ≤0.8 |
| Mn | 0.5-1.0 | 0.5-1.0 | 11.0-18.0 | ≤2.0 |
| Cr | 12.0-30.0 | 11.0-30.0 | 1.5-2.5 | 1.5-10 |
| S | ≤0.04 | ≤0.04 | ≤0.04 | ≤0.15 |
| P | ≤0.06 | ≤0.06 | ≤0.06 | ≤0.15 |
| Mo | 0.1-3.0 | 0.1-3.0 | ≤1.0 | ≤0.1 |
| Cu | 0.1-1.0 | 0.1-1.0 | - | - |
| Ni | 0-0.3 | 0-0.3 | - | 3.3-10 |
| Re | - | - | - | - |
Equivalent
Specification | GB/T8263-1999
AS2027 Cr27
AS2027 CrMo 15/3
AS2027 CrMo 20/2/1
ASTM A532 Class Ⅲ Type A 25%Cr
ASTM A532 Class Ⅱ Type B 15%Cr-Mo
BS 4844 3E
DIN1695
NFA32401 | GB/T5680-1998
DL/T 681-1999
JIS G 5153-1999
ASTM A128
DIN GX120Mn12
AFNORZ120Mn12 | GB/T8263-1999
AS2027/Ni-Cr1-550
AS2027/Ni-Cr2-500
AS2027/Ni-Cr4-500
AS2027/Ni-Cr4-600
AS2027/Ni-Cr4-630
ASTM A532 1-A,B,C,D
ASTM A532 2-A,B,C,D,E
ASTM A532 3-A |
| Material Type | Martensite Matrix | Austenitic Mn Steel | - |
| Hardness | HRC≥56 | HB≤300 | HRC≥56 |
| Impact Value | AK≥4J | AK≥80J | - |