Outer Bucket High Cr Skeleton Metal Casting Hardness More Than HRC60
Summarization
High Cr white iron material possess a combination of superior abrasion resistance and a reasonable
degree of toughness. The high Cr castings have longer service life than the other material,such as
high Mn steel and Cr-Mo alloy steel.And now it is widely used in the working condition of high wear and low impact,such as dry grinding process,coal mills,cement mills due to its excellent performance.
Specification
| Model Number | DF788 |
| Material | High Cr Cast Iron |
| Hardness | More than HRC60 |
| Dimension | As per drawing |
| Casting Process | Sand Casting |
| Heat Treatment Process | Quenching and Tempering |
| Impact Value | ≥AK10J |
| Inspection | Dimensional Inspection Chemical Composition Inspection Hardness Inspection UT Test |
| Application | Coal Mill,Cement Mill,Mining Industry etc. |
| MOQ | 2Tons |
| Delivery Time | Depends on the quantity to be ordered. |
| Port | Shanghai |
| Package | Steel Pallets |
| Payment Terms | T/T,L/C |
Product Photo
Technical Parameters
| Item | High Cr White Iron | High Cr Alloy Steel | High Mn Steel | Ni-hard Cast Iron |
| C | 2.4-3.2 | 1.1-2.2 | 0.9-1.3 | 2.4-3.6 |
| Si | 0.6-1.2 | 0.6-1.2 | ≤0.8 | ≤0.8 |
| Mn | 0.5-1.0 | 0.5-1.0 | 11.0-18.0 | ≤2.0 |
| Cr | 12.0-30.0 | 11.0-30.0 | 1.5-2.5 | 1.5-10 |
| S | ≤0.04 | ≤0.04 | ≤0.04 | ≤0.15 |
| P | ≤0.06 | ≤0.06 | ≤0.06 | ≤0.15 |
| Mo | 0.1-3.0 | 0.1-3.0 | ≤1.0 | ≤0.1 |
| Cu | 0.1-1.0 | 0.1-1.0 | - | - |
| Ni | 0-0.3 | 0-0.3 | - | 3.3-10 |
| Re | - | - | - | - |
Equivalent
Specification | GB/T8263-1999
AS2027 Cr27
AS2027 CrMo 15/3
AS2027 CrMo 20/2/1
ASTM A532 Class Ⅲ Type A 25%Cr
ASTM A532 Class Ⅱ Type B 15%Cr-Mo
BS 4844 3E
DIN1695
NFA32401 | GB/T5680-1998
DL/T 681-1999
JIS G 5153-1999
ASTM A128
DIN GX120Mn12
AFNORZ120Mn12 | GB/T8263-1999
AS2027/Ni-Cr1-550
AS2027/Ni-Cr2-500
AS2027/Ni-Cr4-500
AS2027/Ni-Cr4-600
AS2027/Ni-Cr4-630
ASTM A532 1-A,B,C,D
ASTM A532 2-A,B,C,D,E
ASTM A532 3-A |
| Material Type | Martensite Matrix | Austenitic Mn Steel | - |
| Hardness | HRC≥56 | HB≤300 | HRC≥56 |
| Impact Value | AK≥4J | AK≥80J | - |